한국주조공학회

In this study, in order to improve the lifespan of parts made of manganese steel, manganese steel was cast by varying the amount of Ti added to the steel. In order to confirm the characteristics of the cast material, processing characteristics including tensile and surface characteristics and bearing ratio were investigated. It was confirmed that when the amount of Ti added to high manganese steel exceeds 0.5%, the strength of the alloy is improved due to grain refinement, and fine carbides are formed inside the steel. This results in increased resistance to surface wear compared to the alloy with only Mn added. There was no significant difference in the increase in tensile strength as the Ti content in manganese steel was increased. However, inclusion of Ti showed a small but greater effect on wear resistance compared to Mn, and the size and the distribution of carbides become coarse depending on the Ti content. and was evenly distributed. It was confirmed that the strength and surface properties of manganese steel can be improved by the addition of Ti to improve the lifespan of parts made with this steel. It was found that Ti is effective in developing materials with excellent wear resistance due to refinement of dendrite crystal grains. In the samples where Ti was added, the carbide appears to increase the resistance to surface roughness, and due to the nature of Mn steel, surface hardening begins to occur, which appears to extend the life.

Manganese steel, Tensile properties, Surface properties, Titanium and Cast steel.